Titanium plate manufacturing process

　　Hot forging is a forging process carried out above the recrystallization temperature of metal.

　　Hot rolling is a rolling process carried out at a temperature higher than the recrystallization temperature.

　　The cold rolling process in which the plastic deformation temperature is lower than the recovery temperature.

　　Annealing: a metal heat treatment process in which metal is slowly heated to a certain temperature, maintained for a sufficient time, and then cooled at an appropriate speed (usually slow cooling, sometimes controlled cooling).

　　Pickling: immerse the workpiece in an aqueous solution such as sulfuric acid to remove oxide and other films on the metal surface. It is the pretreatment or intermediate treatment of electroplating, enamel, rolling and other processes.

　　Characteristics of titanium plate

　　1. Titanium seed plate is an oxide film on the surface, which is equivalent to a good durable and wear-resistant hair separation agent. The use of titanium seed plate saves the separation agent, makes the electrode plate peel easily, and eliminates the pretreatment process of seed plate. Titanium seed plate is half lighter than copper seed plate.

　　2. The service life of titanium seed plate is more than 3 times that of copper seed plate, which can reach 10 to 20 years according to operating conditions

　　3. Electrolytic copper prepared from titanium seed plate has dense crystal structure, flat and smooth surface and excellent quality.

　　4. Since the titanium seed plate does not need to be coated with separation agent, the pollution of copper electrolyte can be avoided.

　　5. Improve the production capacity and reduce the production cost of electrolytic copper, so as to have better economic benefits.